Heatshrink

Adhesive Lined

Description:

This is a flexible, flame retarded heat-shrinkable polyolefin tubing, with

a shrink ratio of 4 : 1 with a thick wall adhesive which melts and flows,

to seal components contained within. Recommended for applications

requiring water-proofing for light cable and wire harnesses and protection

of connector components.

Features :

• EPA method 3050B

: 1996 other acid digestion

• BSEN1122

: 2001 method B other acid digestion

• EPA method 3052B

: 1996 other acid digestion

• EPA method 3060 and EPA 7196A

: 1992

• Atomic absorption spectrometer / inductively coupled plasma atomic emission spectrometer (ICP + AES) UV-VIS

spectrophotometer

Characteristics:

Operating Temperature

: -55°C to +125°C

Minimum Shrink Temperature

: 70°C

Shrink Ratio

: 3:1 and 4:1

Standard Colour

: Black

(Other colours are also available on request)

Applications:

Manufactured by co-extrusion of polyolefin and hot-melt adhesive. Designed to provide both insulation and sealing for the

protected items. Typically uses are the protection of automotive wires, bundled wires and metal tubes against water and

moisture. The high expansion ratio makes it possible to repair most damaged cable jackets without removing connectors.

Property

Test Method

Typical Data

Tensile Strength

ASTM D 2671

10.4Mpa

Ultimate Elongation (%)

30

Longitudinal Shrinkage (%)

UL 224

0 to -10

Heat Aging

Ultimate Elongation (%)

158°, 168hr

200

Flammability

VW-1

Pass (outer jacket only)

Dielectric Strength (kv / mm)

IEC 243

20

Volume Resistivity (ohm-cm)

UL224

1 × 1014

Copper Stability

ASTM D 2671

Pass

Corrosion

UL224

No corrosion

Technical Data: